標準號：DIN EN 12814-4-2018
中文標準名稱：熱塑性半成品焊接接頭試驗. 第4部分: 剝離試驗; 德文版本EN 12814-4-2018+AC-2018
英文標準名稱：Testing of welded joints of thermoplastics semi-finished products - Part 4: Peel test; German version EN 12814-4:2018+AC:2018
標準類型：J33
發布日期：1999/12/31 12:00:00
實施日期：1999/12/31 12:00:00
中國標準分類號：J33
國際標準分類號：25.160.40
引用標準：EN 1555-3-2010;EN 12201-3-2011;EN 14728-2005;CEN/TS 16892-2015;ISO 5893-2002;ISO 13954-1997;ISO 13955-1997
適用范圍：This European Standard specifies the dimensions, the method of sampling and the preparation of the test specimens, and also the conditions for performing the peel test perpendicular to the weld in order to determine the peel resistance and the failure behaviour. A peel test may be used in conjunction with other tests (e. g. tensile creep, macroscopic examination, etc.) to assess the performance of welded assemblies, made from thermoplastics materials. Peel tests are applicable to overlap welded assemblies made from thermoplastics materials. The T-peel test as defined in Clause 5 will be used only for assessing welded sheet assemblies. This test is not applicable to welded test pieces containing sheets of different nominal thickness. The decohesion test as defined in Clause 6 will be used only for assessing electrofusion joints with nominal thickness of pipe/fitting greater than 10 mm. For socket fusion and for electrofusion socket joints with nominal outside diameter less than or equal to 90 mm, a crush test will be used, as defined in Clause 7. The crush test can also be used for electrofusion joints with outside diameters greater than 90 mm. The crush test for electrofusion saddle joints will be performed in accordance with ISO 13955 [6]. NOTE A decohesion test is also defined in ISO 13954 [5]. The tests defined in this standard should not be used for assessment and/or qualification of thermoplastics fittings, e. g. polyethylene fittings according to EN 1555-3 [1] and EN 12201-3 [2], because they already have their own requirements.